13549213581 肖生

 

医疗级ISO 10993 COC, DMF 12132, USP 第VI类, FDA食品接触, 无 BPA, 薄膜, 袋子

 

TOPAS® 7010F-600

环烯烃共聚物

Topas Advanced Polymers, Inc.

Technical Data

 

产品说明

Product Description

TOPAS 7010F-600 is a robust film extrusion grade designed for blending with polyethylene (PE). It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.

 

Selected Applications

• Forming films (header bags, etc.) 

• Protective packaging 

• Shrink films and labels 

• Twist films 

• Decorative sheet 

• Food packaging 

• Food contact 

 

Leading Attributes

• Clarity, forming, barrier, purity, halogen-free 

• Stiffness for downgauging, improved forming 

• High shrink, low stress, gloss, toughness 

• Outstanding deadfold, clean cutting 

• Stiffness, chemical resistance, forming, even draw 

• Not manufactured with BPA, phthalates, or halogens 

• Broad regulatory approval 

 

Related Grades for Packaging and Film Extrusion

• TOPAS 8007F-04 - ultimate clarity extrusion grade 

• TOPAS 8007F-600 - robust clarity extrusion grade especially for PE blends 

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Topas Advanced Polymers, Inc.

•  TOPAS®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

• 纯度高 • 耐化学性良好 • 无 BPA

• 防潮 • 韧性良好

• 无定形的

特性 • 刚性，高 • 食品接触的合规性

• 无卤

• 高光 • 收缩性高

• 中等透明度

• 共聚物 • 通用

• 包装 • 多层薄膜 • 片材

用途 • 薄膜 • 混合 • 食品包装

• 标签 • 流延薄膜 • 通用

机构评级 • DMF 12132 • ISO 10993 • 欧洲 10/1/2011 12:00:00 AM

• FDA FCN 405 • USP 第VI类

形式 • 粒子

加工方法 • 薄膜挤出 • 流延薄膜

• 吹塑薄膜 • 热成型

 

TOPAS® 7010F-600

环烯烃共聚物

Topas Advanced Polymers, Inc.

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 1.02g/cm³ 1.02g/cm³ ISO 1183

熔流率（熔体流动速率） ISO 1133

190°C/2.16 kg 1.8g/10 min 1.8g/10 min

230°C/2.16 kg 10g/10 min 10g/10 min

溶化体积流率（MVR） ISO 1133

190°C/2.16 kg 0.122in³/10min 2.00cm³/10min

230°C/2.16 kg 0.671in³/10min 11.0cm³/10min

吸水率 (饱和, 73°F (23°C)) 0.010% 0.010% ISO 62

薄膜 额定值(英制) 额定值(公制) 测试方法

薄膜厚度 - 经测试 2.8mil 70µm

拉伸模量 ISO 527-3/1

MD : 2.8 mil (70 µm), 铸造薄膜 305000psi 2100MPa

TD : 2.8 mil (70 µm), 铸造薄膜 247000psi 1700MPa

拉伸应力 ISO 527-3/50

MD : 断裂, 2.8 mil (70 µm), 铸造薄膜 7980psi 55.0MPa

TD : 断裂, 2.8 mil (70 µm), 铸造薄膜 7250psi 50.0MPa

伸长率 ISO 527-3/50

MD : 断裂, 2.8 mil (70 µm), 铸造薄膜 3.4% 3.4%

TD : 断裂, 2.8 mil (70 µm), 铸造薄膜 3.4% 3.4%

透氧率 ASTM D3985

73°F (23°C), 2.8 mil (70 µm), 挤塑薄膜, 50% cm³•mil/100in²/at cm³•mm/m²/atm/

RH 63m/24 hr 2524 hr

水气透过率 ASTM F1249

2.8 mil (70 µm), 73°F (23°C), Cast Film, 85% g•mil/100in²/atm/ g•mm/m²/atm/24

RH 0.2424 hr 0.094hr

热性能 额定值(英制) 额定值(公制) 测试方法

玻璃转化温度 172°F 78.0°C ISO 11357-2

光学性能 额定值(英制) 额定值(公制) 测试方法

光泽度 (60°, 2.76 mil (70.0 µm), 铸造薄膜) > 100 > 100 ISO 2813

雾度 (2.76 mil (70.0 µm), 铸造薄膜) > 2.0% > 2.0% ISO 14782

挤出 额定值(英制) 额定值(公制)

挤塑机进料部分 68 到 158°F 20 到 70°C

料筒1区温度 410 到 446°F 210 到 230°C

料筒2区温度 428 到 464°F 220 到 240°C

料筒3区温度 428 到 464°F 220 到 240°C

料筒4区温度 428 到 464°F 220 到 240°C

口模温度 428 到 464°F 220 到 240°C

挤出机螺杆长径比L / D > 28:1 > 28:1

挤压说明

Head pressure: P > 140 bar / 2000 psi; Fine screen packs as needed

Screw speed: RPM > 50% nominal

Screw design:

• Multi-purpose or barrier screw with mixing section 

• Screw diameter > 60 mm / 2.5 inch 

 

Grooved Feed: Hot temperature: 120°C (248°F)

 

 

 

 

 

 

医疗级ISO 10993环烯烃共聚物,医疗级环烯烃共聚物ISO 10993 COC TOPAS® 7010F-600是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123 

13549213581 肖生